Copper Alloy 110/C110/C11000 Electrolytic Tough Pitch (ETP)
Copper Alloy 110/C110/C1100 Electrolytic Tough Pitch (ETP)  is a very pure alloy of copper
(99.9% min. cu). It is a versatile alloy because of its resistance to corrosion, high electrical and thermal
conductivity, and its aesthetic quality. It is used for a variety of projects and applications including
construction, DIY, arts and craft projects, rfi shielding, manufacturing, electrical applications, research and
development and much more.

C110 Data Specifications Manufactured to ASTM B152
Chemical Properties Copper-99.9% (min.) Oxygen-0.05% (max.)
Physical Properties

Density lb/cu in. at 68F-0.322 Thermal Conductivity 226 BTU- /sq.ft./hr/F Electrical Resistivity 10.3 ohm circ mils/ft Electrical Conductivity (annealed) 101% IACS Modulus of Elasticity 17,000,000 psi Coeff of Thermal Expansion 68-572 Fahrenheit 9.8PPM/Fahrenheit

Mechanical Properties Tensile Strength Yield Strength1 Elongation2 Temper-Annealed  26 to 38 ksi 6 to 13 x 1000 psi 20-50

Annealing-This alloy can be annealed between 700 and 1200 degrees Fahrenheit Hot Treatment-1400-1600 Fahrenheit Melting Point (approx.) 1981 Fahrenheit
Fabrication Information

Soldering-excellent Brazing-Good Oxyacetylene Welding-not recommended Gas Shielded Arc Welding-fair Coated Metal Arc Welding-not recommended Spot Weld-not recommended Seam Weld-not recommended Butt Weld-good Cold worked capability-excellent Hot Formed Capability-excellent Forgeability Rating-65 Machinability Rating-20

1 0.2% offset 2 % in 2 inches

This information is for reference only. Basic Copper Inc. provides this information without obligation or liability.